PROPERTIES | VALUES | RULES |
Density | 1.19 g/cm3 | ISO 1183-1:2012 Method A |
Rockwell Hardness | 112L | ISO 2039-2:1999 |
Tensile Modulus | 3150MPa | EN ISO 527:2012 |
Tensile Strength | 80.0MPa | EN ISO 527:2012 |
Tensile Strain at Break | 3.2% | EN ISO 527-1:2012 |
Water Absorption | 0.20% | ISO 62:2008 Method 1 |
Total Luminous Transmittance | 93.4% | ISO 13468-1:1996 |
Vicat Softening Temperature | 105℃ | ISO 306:2013 Method B50 |
Light Ageing Test- UV Exposure | Grey scale: 5 | ISO 4892-3:2016 Cycle 1 |
Mean Coefficient of Linear Thermal Expansion | 72×10-6 K-1 | ISO 11359-1:2014 |
Compressive Stress at Yield | 129MPa | EN ISO 604:2003 |
Flexural Strength | 120MPa | ISO 178:2013 |
Compressive Yield Strength | 111MPa | ASTM D695-15 |
Compressive Modulus | 3450MPa | ASTM D695-15 |
Shear Strength | 59.7MPa | ASTM D732-17 |
Deflection Temperature under Load | 100.2℃ | ASTM D648-18 Method B |
Modulus Elasticity | 2810MPa | ASTM D695-15 |
Raw materials | 100% virgin of Lucite MMA materials | |||||
Thickness | 30-150mm one time casting, 150-950mm mm Multi-plate composite overlay | |||||
Color | Transparent(transparent 93%) of cast acrylic panel | |||||
MOQ | 1 PCS acrylic panel/curve/tunnel/L shape acrylic panel | |||||
Below molding sizes are for your reference. Please note that: below size (molding size) ≠ panel net size | ||||||
Size | Thickness | Size | Thickness | |||
1300x2500mm | 30-70mm | 1350x2650mm | 30-100mm | |||
1450x2700mm | 30-100mm | 1600x2600mm | 30-100mm | |||
1650x3150mm | 30-100mm | 2200x3200mm | 30-110mm | |||
1650x3500mm | 30-100mm | 2750x4250mm | 30-130mm | |||
1800x5000mm | 30-150mm | 2100x5500mm | 30-150mm | |||
3000x6200mm | 50-250mm | 3000x6700mm | 50-250mm | |||
3000x8200mm | 80-250mm | 3000*8700mm | 80-250mm | |||
3000x11500mm | 100-250mm | 3700x8100mm | 120-300mm | |||
Generally, Our factory introducing the use of acrylic panels into architectural project such as oversize aquarium,outdoor swimming pool and water feature. |