HuiZhou AUPOOL Technology Co.LTD
HuiZhou AUPOOL Technology Co.LTD
Add to Cart
NO. | Physical Property | ISO | Unit | Result | ||||
1. | Specific gravity / density | D792 | Kg/m | 1175 | ||||
Optical | ||||||||
2. | Luminous Transmittance | GB/T2410-2008 | % | 92.6 | ||||
3. | Haze | GB/T2410-2008 | % | 1.8 | ||||
Mechanical | ||||||||
4. | Tensile Strength | 527-2:2012 | ||||||
a) Maximum tensile strength | MPa | 80.7 | ||||||
b) Elongation at break | % | 4 | ||||||
c)Tensile modulus | MPa | 3010 | ||||||
5. | Flexural Strength | 178:2010 | ||||||
a) Maximum flexural strength | MPa | 87.7 | ||||||
b) Maximum flexural strength | MPa | 2900 | ||||||
6. | Comintsane Yield Stress | 604:2002 | MPa | No Yield Point | ||||
7. | Izod Notched Immpact Stress | D256-10 (Method c) | J/m | 8 | ||||
8. | Shear Strength | D732-10 | MPa | 62.5 | ||||
9. | Rockwell Hardness | 2039-2:1987 | HRL | 105 | ||||
Thermal | ||||||||
10. | Flammability | UL94-2013 (7) | mm/min | 24.1 | ||||
11. | Heat Deflection Temperature | 75-2:2013(Method B) | °C | 106.2 | ||||
12. | Glass Transition Temperature | 11357-2:1999 | ||||||
a)Teig | °C | 105.6 | ||||||
b)Tmg | °C | 114.0 | ||||||
c)Tefg | °C | 122.3 | ||||||
13. | Coefficient of Linear Thermal Expansion | 11359-2:1999 | °C | -40 to 110 | ||||
a)Parallel to flow | um/m-°C | 78.60 | ||||||
b)Perpendicular to flow | um/m-°C | 80.56 | ||||||
Others | ||||||||
14. | Water Absorption | 62:2008 | % | 0.12 | ||||
15. | Odor | None | ||||||
16. | Taste | None | ||||||
Product Name | Acrylic pool | Shape | Customer's Demand |
Brand | AUPOOL | Color | Clear/transparent |
Material | Lucite Acrylic | Place of Product | Guangdong Province,China |
Surface | High Surface Hardness | Modes of packing | PE film masking on both sides,KT board and angle iron. |
Thickness | 20-950 mm customized | Light transmission | High light transmission(93%) |